Clay brick

Detailed introduction

Clay brick, also known as sintered brick, is a small man-made building blocks, clay brick (including shale, gangue and other powder) as the main raw material, through mud treatment, molding, drying and roasting, solid and hollow separately.
classification
According to the void ratio: solid brick (no or less than 25% of the void ratio of brick), porous brick (void ratio equal to or greater than 25%), hole size small and large number of bricks, often used in load-bearing parts, high strength grade. Hollow bricks (bricks with a void ratio equal to or greater than 40% and large and small voids, often used in non-load-bearing areas, with low strength levels).
Characteristic
Solid brick and perforated brick are mostly used for load-bearing structure walls, and hollow bricks are mostly used for non load-bearing structure walls.
Advantage introduction
Clay brick is made of clay (including shale, gangue and other powder) as the main raw material, through mud treatment, molding, drying and roasting.
During the Spring and Autumn Period and the Warring States Period, China successively created square and rectangular bricks. In the Qin and Han Dynasties, brick-making technology and production scale, quality and variety of patterns have been significantly developed. The size of ordinary bricks is 240 mm *115 mm *53 mm. According to the compressive strength (Newton/square millimeter, N/mm2), they are divided into six strength grades: MU30, MU25, MU20, MU15, MU10 and MU7.5. Clay brick is widely used in civil engineering because of its low price, durability, fire protection, heat insulation, sound insulation, moisture absorption and other advantages. Scrap bricks can also be used as aggregate for concrete. In order to improve the shortcomings of ordinary clay brick, such as small size, self-weight and high soil consumption, it is developing towards the direction of light weight, high strength, hollow and large block. The lime-sand brick is made of lime, quartz sand, sand or fine sandstone in proper proportion, which is ground, mixed with water, pressed and cured by autoclave. Fly ash brick is made of fly ash as the main raw material, mixed with coal gangue powder or clay and other cementing materials, through mixing, molding, drying and roasting. It can make full use of industrial waste residue and save fuel.
China's clay brick Al2O3 content is generally more than 40%, Fe2O3 content is less than 2 to 2.5%. The clinker is 65 to 85%, and the clay is 35 to 15%. The crushed bonded clay and fine clinker are mixed and grinded, and then mixed with granular clinker to make semi-dry mud. The semi-dry mud is formed under high pressure and fired at about 1400 C. The performance is good. The clay brick is weak acidic at high temperature, and its resistance to alkaline slag corrosion is slightly poor, but it increases with the increase of Al2O3 content. Thermal stability is better than silica brick, magnesia brick (see magnesia brick) and so on.
The qualified clay bricks of blast furnace were dried and impregnated with phosphoric acid in vacuum and sintered at low temperature twice. The products were used for lining the upper part of blast furnace body.

 Main Properties


Index

Brand name


N-1

N-2a

N-2b

N-3a

N-3b

N-4

Refractoriness ℃≥

1750

1730

1730

1710

1710

1690

1400

1350

1320

1300



Reburn line change%

1400℃×2h

+0.1
-0.4

+0.1
-0.5

+0.2
0.5

1350℃×2h

+0.2
-0.5

+0.2
-0.5

+0.2
-0.5

Apparent stomatal rate % ≤

22

24

26

24

26

24

Pressure resistance MPa ≥

30

25

20

20

15

20

 

粘土砖


Prev:None
Next:Insulating brick

 E-mail:glgs1994@163.com

冀ICP备05015860号-1  

1540776817699677.png


Copyright © http://www.sd-naracom.com/en/ 万搏manbext官网登录 Specializing in Custom made refractories,Hebei refractories manufacturer,Construction of refractory materials in Hebei ,Welcome to inquire!

1540776817699677.png

0315-3384573

扫一扫

1536884200741652.jpg

关注公众号